Abstract:
It is difficult to process advanced materials such as composites with conventional processes to
attain desired properties. Thus, non-conventional material processing techniques have gained
popularity to develop composite materials. In the today’s scenario, demand of advanced
materials to achieve high specific strength in aerospace industry and automobile sector is
increasing, which motivates researchers to develop tailored materials and advanced processing
techniques. In recent time, magnesium matrix composite are being researched for enhanced
properties due to its lower weight. In the present work, an overview on different processing
techniques used for development of magnesium matrix composite processed was studied. The
merits and demerits of the different processes have been compared to understand ease of
composite processing. A new composite process technique using microwave energy at 2.45
GHz frequency was explored. Microwave sintering was carried out for magnesium based metal
matrix composite having reinforcement in amount (5%, 10% & 15% by weight) of SiC powder.
Characterization for microstructures was performed using SEM/FESEM, optical microscope,
EDS analysis. From optical micrograph, SEM images and EDS analysis, it was found that on
increasing the amount of SiC particles in AZ91 alloy more Mg2Si and SiC phases were
appeared in the sintered samples.
Physical property i.e. density was measured using Archimedes principle and micro hardness
test was performed to measure microwave sintered samples. Experimental density of the
sintered samples were in the range of 85 to 90% of the theoretical density and micro hardness
was more in sintered sample which had 5% SiC particle by weight.
Moreover, all the results obtained from all analysis have been discussed. Subsequently,
attention was focussed on the challenges in the proposed method and yield of the process.
Future scope for the microwave sintering of magnesium based metal matrix composite is also
outlined.